VON | BIS | Temperatur | Literatur | |
Wärmeleitfähigkeit | Wärmeleitfähigkeit | t (°C) |
| |
λ (W/(m*K)) | λ (W/(m*K)) |
|
| |
Aluminium | 230 | 230 | -100 | [1] |
Aluminium | 220 | 220 | 0 | [1] |
Aluminium | 205 | 205 | 200 | [1] |
Aluminium | 193 | 193 | 400 | [1] |
Duraleminium | 165 | 165 | 20 | [1] |
Antimon | 22,53 | 22,53 | 20 | [3] |
Blei | 35 | 35 | 20 | [2] |
Bronze CuZn32 | 58,15 | 58,15 | 20 | [3] |
Chrom | 86 | 86 | 20 | [1] |
Edelstahl Monel 505 | 20 | 20 | 20 |
|
Edelstahl V2A | 21 | 21 | 20 | [1] |
Gold rein | 295 | 295 | 20 | [1] |
Graphit | 140 | 140 | 20 | [3] |
Grauguss | 48,8 | 48,8 | 20 | [3] |
Kupfer | 380 | 380 | 20 | [2] |
Handelskupfer | 372 | 372 | 20 | [1] |
Magnesium | 159 | 159 | 20 | [1] |
Messing | 81 | 105 | 20 | [3] |
Messing MS60 | 113 | 113 | 20 |
|
Neusilber | 29 | 29 | 20 |
|
Nickel | 52 | 52 | 20 | [3] |
Platin | 71 | 71 | 20 | [1] |
Silber | 429 | 429 | 20 | [3] |
Silber | 426 | 426 | 100 | [3] |
Stahl | 46,5 | 46,5 | 20 |
|
Stahl 0,2%C | 50 | 50 | 20 | [2] |
Stahl 0,6%C | 46 | 46 | 20 |
|
Stahl 8% Ni | 21 | 21 | 20 |
|
Stahl legiert | 15 | 15 | 20 | [2] |
Stahlguss | 52 | 52 | 20 | [3] |
Titan | 16 | 16 | 20 | [1] |
Weißmetall | 35 | 70 | 20 |
|
Wismut | 10 | 10 | 20 | [1] |
Wolfram | 197 | 197 | 20 | [1] |
Zink | 109 | 109 | 20 | [1] |
Zinn | 63 | 63 | 20 | [1] |